Aluminum Ramp and Platform Fabrication: Mobile Welding

Aluminum ramps and platforms earn their keep where downtime hurts most: at loading docks, on trailers that move heavy equipment, and around industrial sites that live on tight schedules. Fabricating and installing them on site, with a mobile welder who knows aluminum inside out, shortens that downtime and avoids the expensive shuffle of hauling gear to a shop. The work looks simple from a distance, yet the details decide whether a ramp holds up to forklifts and weather or twists itself loose by the next season.

I have spent enough days with a portable welder in the back of a truck, TIG torch in one hand and a tape measure in the other, to know the difference. The right alloy, the correct joint prep, and a layout that anticipates how people actually use the equipment, these are the pieces that make a ramp or platform feel invisible and reliable. What follows draws on that field experience, not just spec sheets.

Where aluminum makes sense, and where it does not

Aluminum pays off when weight matters and corrosion is a threat. Portable ramps, fold-out trailer ramps, and platforms in coastal or chemical environments are prime candidates. A 6061-T6 extruded tread plate deck with 2 inch channel stringers moves easily with two people, resists salt, and keeps the slip risk low. It will not rust like carbon steel, and you can keep it clean without paint.

There are trade-offs. Aluminum has about one third the stiffness of steel for the same geometry. If you match a steel ramp thickness with aluminum, it will flex more under the same load. The fix is simple but often missed: increase section depth, not just thickness. Swapping a 3 inch steel channel for a 4 inch or 5 inch aluminum channel, or using a truss-like web of square tube beneath the deck, brings deflection back in line. Heat also softens aluminum in the heat affected zone, so weld placement and post-weld geometry matter more than in stainless or structural steel. If you need very high point load resistance, for example a compact track loader crossing a lip with one track, you design for that with reinforcement plates and wide load spreaders.

For purely decorative items, like wrought iron fencing or ornamental gates, aluminum can look out of place. For structural, constantly loaded ramps feeding an industrial press line, steel may still win. You can mix materials too, for instance aluminum ramp panels with stainless hinges and carbon steel embeds set in concrete.

Codes, certifications, and loads that actually show up

Most ramps and platforms fall under general OSHA walking-working surface rules and, where public access exists, ADA slope and handrail guidance. Industrial platforms near heavy equipment or a loading dock often specify IBC or ASCE load criteria. A reasonable starting live load for a service platform is 60 to 100 pounds per square foot, with concentrated loads of 300 to 1,000 pounds at any point on the deck. Vehicle ramps need more, and it pays to translate your real use into numbers. A pallet jack loaded with a 2,200 pound pallet puts two small wheels under the entire weight. That gives you roughly 1,100 pounds per wheel on a footprint the size of a credit card. Aluminum handles it if you spread the load through ribbed decking or additional stringers at the wheel paths.

Where inspection or insurance requires, an AWS certified welder with aluminum procedures on file should do the work. Many jobs call for D1.2 structural aluminum or, for mixed metal work around a plant, D1.1 for steel and D1.6 for stainless. If someone says they are certified, ask which code, which positions, and whether the procedure includes the joint types your project needs. A certificate alone does not cover the details of a flange weld on a 5xxx deck plate or the fillet welds along a 6xxx channel. Good mobile welding businesses keep WPS and PQR paperwork ready and can share it without a song and dance.

Alloy, temper, and filler choices that avoid headaches

Most field-fabricated ramps and platforms use 6061-T6 for structural members. It machines cleanly, holds threads, and is readily available in channels, angles, square tube, and plate. For deck surfaces where slip resistance and corrosion resistance matter, 5052-H32 tread plate often outperforms 6061. It bends well, does not crack at the diamonds, and resists salt. The catch is welding across different alloys and tempers. If you weld 6061-T6, expect strength loss in the heat affected zone adjacent to the weld. Designing with a higher section modulus and moving welds away from peak stress points preserves capacity.

Filler selection matters. ER5356 is the workhorse for 5xxx and 6xxx base metals in a structural context, especially outdoors or near chlorides. It offers better crack resistance than ER4043, better color match after anodizing, and higher as-welded strength in many joints. ER4043 has its place, typically for 6xxx to 6xxx where fluidity is helpful and the joint is not highly stressed. For anodized, visible work like railings, 5356 keeps the weld from turning gray after finishing. For food-related stainless steel welding nearby, keep aluminum spatter away, and clean tools separately to avoid cross-contamination.

TIG vs MIG in the field

Both TIG and MIG weld aluminum well, but their strengths differ. TIG gives control and clean, small beads. On thinner deck skins or visible rail-to-post joints, TIG shines. MIG, with a push-pull gun or spool gun, delivers speed and consistent penetration on thicker sections like 1/4 inch channel flanges or 3/16 inch square tube stringers. In mobile welding, wind and power availability frame the choice. TIG hates wind and dirty power. A truck welding rig with a steady generator and a fabric wind break makes TIG practical, but on a busy loading dock with forklifts buzzing, MIG with a stout gas flow and a shield often wins.

For MIG, 100 percent argon is standard for aluminum. Flow rates around 25 to 35 CFH work outside if you build a wind shadow. For TIG, keep the tungsten clean, often 2 percent lanthanated sharpened to a small flat, with AC balance tuned to the oxide layer you see. Start with more cleaning action on cast or dirty extrusions, then taper toward penetration as the puddle wets out. Preheat can help on thick wrought shapes, 200 to 300 F is common, but avoid overcooking the temper.

Field measurement and layout that save rework

Accurate layout prevents the oh-no moment when a ramp lands an inch shy of a trailer lip or the platform door swing hits a guardrail. I measure from fixed references, not surfaces that might warp under welding heat. On trailers, hitch to axle centers and the top of the coupler do not move. On a concrete loading dock, take elevations from plate marks on the wall and laser levels checked against a known benchmark. When the client says their trailer deck height is 34 inches, verify under load. Springs settle, and 34 inches empty can be 32.5 inches with a forklift on it.

Slope is not negotiable if foot traffic is involved. For ADA-compliant ramps, plan for a slope not steeper than 1:12 with level landings. For equipment ramps, slope depends on clearance and traction. Many forklifts prefer 1:8 or flatter. Add a foot for every inch you shave off the slope if you want a ramp that everyone will use without cursing.

Edge conditions call for careful attention. The interface between ramp and trailer or dock often takes the highest stress. A stainless steel hinge with grease fittings keeps motion smooth and tolerates corrosion better than plain steel. If you choose an aluminum piano hinge for weight, increase thickness and add dowel pins to prevent the knuckle from tearing under impact. Where a removable ramp hooks to a receiver, use a captured pin system with replaceable wear bushings. These bushings are cheap insurance compared to repairing elongated holes in the main frame.

Joint design to resist real-world abuse

Fatigue, not ultimate strength, kills many aluminum ramps. Repetitive loading from dollies and pallet jacks produces micro cracks at weld toes, especially where stiffeners terminate. Avoid abrupt transitions. Taper gussets and end them away from peak stress zones. Add cope holes at the ends of cutouts to avoid sharp corners. Where a stiffener meets a flange, use a radius, not a square end. Stitch weld deck plates rather than continuous welds in non-critical areas to reduce heat input and minimize distortion.

Bimetallic contact brings galvanic corrosion into the picture. Aluminum bolted to a carbon steel embed at a dock will corrode rapidly if water and salts get between them. Insulate the interface with non-conductive shims, paint the steel, and use stainless hardware with nylon washers. If you must weld aluminum to steel, you cannot do it directly with standard aluminum welding. Use mechanical fasteners or explosion-bonded bi-metal transition inserts designed for welding on one side and bolting or welding steel on the other.

Decking, traction, and weather

Deck surface choices shape safety. Standard 1/8 inch or 3/16 inch 5052 tread plate provides decent slip resistance. In wet or icy conditions, consider serrated bar grating or extruded aluminum plank with integrated ridges. Grating drains and sheds snow, which matters on open trailers or exterior platforms. Where small wheels need a crack-free surface, solid plate with bonded or spray-on grit works better. If chemicals or food processing rinse-downs are part of the environment, avoid coatings that soften under solvents. Stainless fasteners and sealed seams stop water from wicking under the plate and corroding the hidden side.

Rain blows sideways into the best of designs. If a platform sits outdoors, slope the deck slightly, around 1 to 2 percent, to shed water, even if the main ramp slope is steeper. Provide drip edges on the underside of overhangs. For interior loading docks that see condensation, specify sealed, non-skid nosings at edges and add touch-up instructions for the grit coating. People slip at transitions, not in the middle of a ramp.

Handrails and edge protection

Railings turn a good ramp into a safe one. OSHA and IBC proportions differ, but field sense helps. Set the top rail where a tall person naturally rests a hand, usually 42 inches in industrial settings. Mid-rails or infill keep people from falling through. On aluminum, 1-1/2 inch schedule 40 pipe or 1-1/2 inch square tube feels sturdy without looking bulky. Weld rail joints with TIG when visibility matters, grind smooth, then rub with Scotch-Brite for a consistent grain. For removable rails on a trailer, use stainless steel receivers welded to the aluminum frame with isolation shims and 5356 filler, then pin the rails with spring clips for quick changes.

Toe boards are not glamorous until a wrench rolls off a platform toward someone’s head. A 4 inch toe board along the open edges of industrial platforms keeps tools contained. Fasten toe boards mechanically so they can be replaced when forklifts clip them, and leave small gaps for drainage at low points.

Fasteners, hinges, and mixed-metal strategy

Hardware fails long before good welds if you choose the wrong metals. Stainless fasteners, typically 316 in corrosive spots and 304 elsewhere, play well with aluminum if you break the galvanic circuit. Nylon washers and sleeves prevent direct contact, and a corrosion-inhibiting paste on threads helps. Avoid zinc-plated steel hardware touching bare aluminum outdoors. If you must use carbon steel for a heavy-duty hinge pin, isolate it and keep it greased. For pivot points that will see grit, bronze bushings inside an aluminum knuckle outlast bare aluminum-on-steel contact by years.

Bolted connections on aluminum need proper preload without crushing the base metal. Use washers with larger bearing area or backing plates under bolt heads. Torque values should factor in lubrication and gasket compression. Over-torqued bolts dimple aluminum, which loosens the joint over time.

Fabrication workflow for on site welding services

Most mobile welding projects benefit from a hybrid approach. Prefabricate where precision helps, then finish fit and weld on site. Cut and tack the main frame in the shop with MIG, confirm squareness, and pre-drill for hardware. Add tabs, gussets, and hinge mounts, but leave final holes undersized. Bring the assembly to the site with a portable welder and a modest jig kit: clamps, temporary legs, cribbing, and shims.

On site, align to the real world, not the drawing. Trailers sit at slight angles. Dock faces are rarely perfectly plumb. Use levels, feeler gauges, and packers to set proper gaps at hinges and landings. Tack, load test lightly if possible, then finish weld in sequences that balance heat input. For a long ramp, start welds at the center and work out, flip where possible to stitch both sides, and let sections cool before the next pass. TIG tight, visible joints last. Brush every pass with a stainless steel brush reserved for aluminum to clear oxides before the next bead.

Bring backup power for the welder and a wind solution. A simple collapsible wind wall or canvas blanket can turn a gusty dock into a workable bay. Keep filler rods and wire clean in sealed tubes. Contamination causes more rework than any other single factor on aluminum jobs.

Repair, retrofit, and emergency welder response

Ramps fail from three predictable patterns: hinge tearing at the knuckle, deck plate cracking between fasteners or at stiffener ends, and frame fatigue near the highest stress points. A clean repair involves grinding out the crack to a soft U, drilling a small stop hole at the crack tip, and welding with 5356. Add reinforcement that spreads load, not just a thick patch on top of the same stress riser. Move the start and end of stiffeners, taper them, and, if clearance allows, add a second stringer under wheel paths.

Retrofits on older trailers often start with replacing thin steel flip ramps with aluminum to drop weight and improve corrosion resistance. Keep hinge geometry and balance in mind. A lighter ramp may need a different spring rate or a gas strut to prevent slamming. If the original hinge pin was mild steel riding in a steel tube, shift to stainless pin and aluminum knuckle with replaceable bushings. Insulate the contacts and provide grease ports. For platforms connected to process equipment, coordinate shutdown windows tightly. A well-prepared team can cut out a damaged section, fit a new aluminum frame, and stitch deck plate overnight, so the plant runs by morning.

When a call comes in for a bent ramp after a forklift miscue, the first job of an emergency welder is triage. Determine whether a straightening and a temporary reinforcement can get operations back safely, then plan a permanent fix. Aluminum work-hardens quickly. Cold straightening is possible in small degrees, but large bends often need heat and careful jacking to avoid fresh cracks. Document what you change so the next inspection does not guess at hidden damage.

Surface finishes and long-term care

Raw aluminum holds up well, but finishing can extend life and improve grip. Anodizing looks excellent and improves corrosion resistance, though welded areas take finish differently. If appearance matters, set expectations that welds may contrast slightly after anodize. Powder coating can work, but surface preparation is critical and chips on edges create corrosion traps. For industrial ramps that live rough lives, a Scotch-Brite blend after fabrication and a clear sealant on hand-contact areas give a practical, maintainable finish.

Maintenance is straightforward. Rinse off salts and chemicals, especially near a loading dock where de-icing materials accumulate. Inspect hinges and pins quarterly. Retorque accessible fasteners after the first month of use, then annually. Replace grit coatings when the aggregate wears smooth on the main travel lines. Light corrosion near stainless fasteners usually points to failed isolation or trapped moisture; fix both, not just the symptom.

Case notes from the field

A rental company running equipment trailers asked for lighter ramps that two people could deploy safely. The original steel ramps weighed about 140 pounds each, with 3/16 inch plate skins and angle stiffeners. We built aluminum replacements from 2 by 4 inch 6061 rectangular tube stingers with 5052-H32 tread plate skins. Each ramp landed at 78 pounds. The hinge pins switched to 316 stainless with nylon isolators and grease fittings. We chose ER5356 wire for MIG welds on the frame and TIG for the hinge tabs. After six months, the only service call involved a missing clip, not a crack.

On a coastal loading dock feeding a seafood plant, the client fought rust on their steel platforms and railings. We fabricated aluminum platforms with serrated plank decking and 6061-T6 stringers, tied to stainless embeds cast in new concrete. Handrails used 1-1/2 inch schedule 40 aluminum pipe with TIG welded fittings, then anodized. Every dissimilar contact point received isolators. Three winters later, the rails still bead water. When forklift forks hit the toe boards, we unpinned and replaced the sacrificial aluminum pieces in an hour, with no welding required.

A hospital called on a Sunday for a temporary ADA ramp after an exterior concrete landing settled and left a trip hazard. The space dictated a 1:12 slope with a turn. We built modular aluminum panels in the shop, carried them in on a truck welding rig, and finished fit on site. The panels linked with stainless hardware and nylon shims. We TIG welded the visible corners for a clean look, then added gritted nosings. The ramp served for eight months until the concrete was re-leveled, then moved to another entrance. Design for relocation saved them a second project.

Integrating with fencing, gates, and site constraints

Ramps often tie into fencing and gates. If the site uses wrought iron fencing or existing steel railings, we avoid direct aluminum-to-steel welds. Instead, we set aluminum posts with base plates anchored to concrete, and connect to the steel fence with insulated brackets or a small stainless transition piece. Gate leaves that sit over a ramp benefit from aluminum frames to keep weight down, with stainless hinges and latches. Add a drop-bolt receiver in the ramp deck with a reinforced sleeve to avoid denting, and seal around it so water does not collect.

On industrial sites with pipe racks along platforms, we provide extra clearance and design toe boards and mid-rails to accommodate pipe welding work or pipe repair access later, so maintenance crews do not torch out sections of the railing. Thinking ahead in the layout reduces the urge for field modifications that weaken the structure.

What a solid mobile welder brings to the job

Good on site welding services go beyond the bead. A competent mobile welder shows up with the right power, shielding gas, and consumables for aluminum welding and stainless steel welding, understands the rhythm of a loading dock, and keeps the work area safe for pedestrians and operators. The rig carries clamps, straightedges, stands, a small press for bushings, and enough stock to solve surprises. AWS credentials back the technique, but attitude matters too. If a schedule shift calls for late hours, the work still needs the same cleanup, the same brush between passes, and the same patience with fit-up. No one remembers a fast sloppy job, they remember a ramp that just works.

Quick field checklist for aluminum ramp projects

  • Confirm real-world deck heights, slopes, and clearances under load.
  • Select alloy and filler with corrosion, strength, and appearance in mind.
  • Isolate dissimilar metals at every contact point with shims, coatings, or sleeves.
  • Place welds away from peak stress, taper stiffeners, and manage heat to protect temper.
  • Plan prefabrication and on-site sequences to control distortion and meet shutdown windows.

Budgeting and lifecycle

Aluminum often costs more at purchase than painted carbon steel, sometimes by 20 to 50 percent depending on shapes and market prices. Over a five to ten year window, the maintenance savings usually erase that gap. No repainting, minimal rust repair, and easier handling translate into fewer service calls and less downtime. For trailers, lower ramp weight cuts the back strain risks and, in some cases, frees up payload. For industrial sites, corrosion resistance reduces the constant touch-up grind near wash-down areas or chemical exposure.

If you need stainless accents or high-polish rail sections, add labor time for finish work. TIG on visible joints is slower than MIG structural welds, yet the result justifies it in public-facing spaces. Do not skip the isolation hardware to save a few dollars. Galvanic corrosion will return the bill with interest.

Safety, training, and small habits that pay off

Every job starts with disconnecting battery grounds on vehicles and trailers, moving flammables, and setting a fire watch. Aluminum dust burns impressively. Collect grindings, keep a clean pad, and check under decks for smoldering fibers. Ask operators to park heavy equipment off the work area. A surprise forklift crossing a half-tacked joint tests more than your welds.

Inspection ties to training. Teach the maintenance team to look at weld toes near hinges, at the ends of stiffeners, and around bolted receivers. Slight white oxide blooms around a stainless fastener on aluminum indicate trapped moisture or a missing isolator. A quick fix now avoids a larger repair later. Train staff to report a change in hinge feel. A dry hinge, or one that binds, tells you the bushing or pin is wearing. Grease points exist for a reason.

Closing thoughts from the field

Aluminum ramp and platform work rewards the craftsperson who respects the metal’s quirks. Keep heat down, keep joints smooth, keep dissimilar metals from fighting each other, and think about how people push, pull, and drive across what you build. The payback shows up in quiet equipment, fewer calls at midnight, and the steady confidence of a crew that trusts the ramp under their feet.

If your site needs design help, fabrication, or repair, look for a welder who can speak comfortably about 6061 and 5052, about ER5356 vs ER4043, about TIG and MIG trade-offs, and who has put real time into truck welding in the field. Ask about AWS qualifications, past work on loading docks and trailers, and how they handle emergency welder calls. The right partner brings the shop to your site and leaves behind aluminum work that simply does its job.

On Call Mobile Welding

917 J Pl Suite 2, Plano, TX 75074

(469) 750-3803

I am a dedicated problem-solver with a complete experience in project management. My focus on breakthrough strategies drives my desire to create growing initiatives. In my entrepreneurial career, I have established a reputation as being a daring strategist. Aside from managing my own businesses, I also enjoy counseling entrepreneurial risk-takers. I believe in guiding the next generation of startup founders to achieve their own ideals. I am easily exploring disruptive ventures and joining forces with complementary strategists. Innovating in new ways is my passion. Outside of involved in my business, I enjoy immersing myself in foreign locales. I am also dedicated to continuing education.